Shock and vibration resistance, secondary heat cure

Download TDS

Application Tips

Loxeal-30-30
Applications
  1. Loxeal 30-30 is specially designed for bonding float glass to glass in the manufacturing of glass and crystal furniture with flexibility.
Replaces Solvent Bonding, Ultrasonic Welding
Available pack size 50ml, 250ml, 2litre
Standards ASTM, DIN, REACH, RoHS
Related Accessories
(Click image to explore more)

Specifications

Chemical Composition Urethane metacrylate
Curing Mechanism Polymerization on exposure to UV rays
Recommended substrates Glass/Glass ,Glass/Metal , Transparent Plastics
Recommended UV Waves 365 to 420 nm
Recommended Intensity 100mW/cm²
Curing time 5-10 seconds
Tensile Strength 15 – 25 N/mm²
Service Temperature -55°C to 120°C

Features and Benefits

Loxeal 30-30T has a secondary heat curing mechanism and can be cured at 90°C for about 6min.
The product is colourless and provides fully transparent bondlines.
High operating temperature (120°C)
High elongation post curing, 30-70%

Notes

  • Some users compromise on the wavelength of UV bulb and intensity.It must be noted that for best performance wavelength must be 365-420 nm and intensity of 100mW/cm².
  • Curing time depends on depth of adhesive bondline and must be factored in while calculating production time.