High temperature, surface insensitive

Download TDS

Applications

Application Tips

Loxeal-IS-43S
Applications
  1.  Loxeal 43S is a top selling Cyanoacrylate adhesive widely used in applications such as automotive hose assembly, O-ring bonding, plastic reservoir, bonding of insulation in electric motors, ferrite E core transformer bonding, loud speakers and many more.
Replaces Solvent Bonding, Ultrasonic Welding
Available pack size 20gm, 50gm, 500gm
Standards NSF, ASTM, DIN, ISO, REACH, RoHS
Related Accessories
(Click image to explore more)		 Loxeal-Activator-9-ra Needle-holder-raLoxeal-Primer-7-rametal-nozzles-needles-for-adhesives-ra (1)

Specifications

Chemical Composition Modified Ethyl Cynoacrylate
Curing Mechanism Moisture
Color Clear
Viscosity 80-150 mPa s
Recommended Substrates Bonding of leather, wood and metals
Max Gap Fill 10 – 150 microns
Fixture Time (secs) ABS : 2 – 10, Steel : 5- 20
Shear Strength 15 – 20 N/mm2
Tensile Strength 15 – 25 N/mm2
Service Temperature -50°C/+120°C

Features and Benefits

Loxeal 43S thanks to an exclusive formulation, perfectly fits to bond acidic and porous surfaces such as paper, cardboard, wood, cork.
Proven temperature strength upto 120°C with peaks up to +150°C
NSF P1 approved

Notes

  • Loxeal 43S is a versatile and top selling model globally. It is a multi purpose product suitable for bonding different substrates and in different conditions.
  • Glass is a substrate generally not to be bonded with Cyanoacrylates, however Loxeal 43S provides good performance.
  • In case of usage with PE, PP, HDPE, LDPE Silicone rubbers or PTFE Loxeal Primer 7 is always recommended.

Applications

Loxeal Instant adhesive for demanding industrial and automotive applications

Loxeal IS 43S is a top-selling Cyanoacrylate adhesive widely used in applications such as automotive hose assembly, O-ring bonding, plastic reservoir, bonding of insulation in electric motors, ferrite E core transformer bonding, loudspeakers and many more. The product is surface insensitive and can withstand temperature up to 150 Dec C.