Gel grade rapid cure structural acrylic adhesive

  1. Structural bonding of wear plates to machine beds
  2. Magnet bonding in DC motors
  3. Name plate bonding in CNC machines, hydraulic valves, fuel transfer system, centrifugal pumps, submersible pumps, gear box, ceramic bonding and other machines.
Replaces boltrivetssolderingbrazing
Available pack size 150ml, 300ml
Related Accessories
(Click image to explore more)


Chemical Composition Urethane Methacrylate
Curing Mechanism It cures with Activator 20
Color Blue gel
Mixing ratio by volume No mixing Required
Recommended substrates Metals, Ceramics, Ferrites
Maximum gap fill 0.05 to 0.20 mm
Handling cure time 20-40 seconds
Functional Cure Time 10-20 Minutes
Tensile Strength 20-25 N/mm²
Shear Strength 20-30 N/mm²
Peel Strength 85-100 N/25 mm
Impact Strength 15-25 KJ/m²
Service Temperature -65°C to +165°C

Features and Benefits

Gel formulation
Cures in seconds, suitable for high speed production line
High impact and peel resistance
High temperature resistance


  • No mixing required for curing.
  • Loxeal34-59 cures when it comes into contact with Loxeal Activator 20. Apply Loxeal 344-59 on one surface and Activator on other surface and press the parts together.
  • Best result is obtained when surface gap is about 0.05mm
  • Presence of rough surface or undulations on the parts can affect bonding strength significantly.


Carbon bush to metal bonding with Loxeal Acrylic adhesive

This video demonstrate the application of Loxeal 3459 – two step, fast curing, structural strength, acrylic adhesive for bonding of carbon bush with with ED – coated metal housing in a submersible pump. Loxeal 3459 – can also be used for: Magnet bonding in DC motors